中南工业大学冶金系钟海云副教授继1984年研究成功“碳还原—高温烧结法”新工艺制取高质量电容器级(63V以下)钽粉,在九江有色金属冶炼厂与从化钽铌冶炼厂转产,通过部、省级定型鉴定后,1987年12月23日又研究出“碳还原法制取高压高比容(63V2800μFV/g)钽粉制造新工艺”,通过部级鉴定。该工艺生产的钽粉,其电性能为:比
Associate Professor Zhong Haiyun, Department of Metallurgy, Central South University of Technology Following the successful research of “Carbon Reduction - High Temperature Sintering” in 1984, a high quality capacitor grade (below 63V) tantalum powder was prepared and passed through Jiujiang Nonferrous Metals Smelter and Conghua Tantalum & Niobium Smelter Ministry, provincial-level stereotypes appraisal, December 23, 1987 and developed a “carbon reduction method to create high pressure high specific volume (63V2800μFV / g) tantalum powder manufacturing new technology,” through the ministerial-level identification. The process of tantalum powder, its electrical properties: ratio