摘要：水库坝体的防渗一般取决于材料和坝体混凝土裂缝，新材料新工艺的出现，基本杜绝了材料的不合格现象的出现，而施工条件施工方法不得不当，难免出现混凝土细小裂缝。水利工程混凝土裂缝对水利工程建筑的影响是无法想象的，只有分清混凝土的裂缝种类，根据不同的种类分析出不同的产生原因，根据笔者多年水利工程施工经验，提出了相应的处理方式，总结出一套成熟的施工方法，对提高水利工程施工质量具有十分重要的意义。
关键字：水利工程 混凝土 裂缝 施工
Abstract: The reservoir dam seepage prevention of general depends on the material and dam concrete crack, new material and new technology, the emergence of basic to eliminate the materials of the phenomenon of the unqualified, and construction conditions of the construction method may not be improper, appears unavoidably tiny cracks in the concrete. Water conservancy project of concrete crack water conservancy project construction influence was unthinkable, only distinguish cracking in concrete of the species, according to the different types of a different reason analysis, according to the water conservancy project construction experience for many years, the corresponding treatment way, summarized a set of mature construction methods, to improve the water conservancy project construction quality has the very vital significance.
Key word: Water conservancy；project construction； concrete； cracks
中图分类号：TV 文献标识码：A 文章编号
小型水库建成前以及建成后，混凝土裂缝都会存在，我们对存在的裂缝不能视而不见，更不能对小型的裂缝置之不理，只有认清混凝土裂缝的种类，针对不同的混凝土裂缝，从形成的原因出发，在水库建成之前，施工过程中，以及后期的维护过程中，三个阶段同时努力，才能达到良好的蓄水能力。
1水工混凝土裂缝的分类
1.1收缩裂缝
（1）表面裂缝
大体积混凝土的内部热量向外散发的较慢，而其外表面与外界接触温度散热速度较快，由于其内部和表面的散热速率不一样，在混凝土的表面会产生一种温度梯度，引发表面产生拉应力，内部产生压应力；如果温差产生的表面拉应力超过此时的混凝土极限抗拉强度，就会在混凝土表面产生裂缝，一般出现在混凝土浇筑后的第3-4天。
（2）贯穿裂缝
混凝土在浇筑数天后由于逐渐降温而产生收缩，再加上混凝土硬化过程中拌合水的水化以及胶质体的胶凝等作用，使得混凝土结构开始收缩，由于受到基底或结构本身的约束，也会产生拉应力，当此拉应力超过混凝土此时的极限抗拉强度，在混凝土结构的薄弱区域就可能产生贯穿裂缝，这种收缩裂缝危害较大。 1.2 塑性塌落裂縫
在混凝土浇筑过程中或者在浇筑初步成型时，都会产生一种塑性塌落裂缝。因为在混凝土的成型过程中，其拌合物中的骨料缓慢下沉，水向上浮，此时钢筋上面的混凝土被钢筋支顶，而钢筋两侧及其下方的混凝土产生下沉，导致混凝土沿钢筋表面产生顺筋裂缝。 1.3 水化热裂缝
水化热裂缝多在大体积混凝土中发生。由于混凝土水化热过高，在凝固过程中释放出大量的水化热，致使混凝土内部温度与混凝土表面温度以及外部环境的温度相差较大，加之有结构自身约束存在，从而产生温度和收缩应力，导致水化热裂缝的产生。通常情况下，大体积混凝土当混凝土内部与表面温度超过24℃，混凝土表面温度与环境温度超过15℃时，最高浇筑温度大于27℃时，则易出现水化热裂缝。 1.4 干缩裂缝
该裂缝多出现在混凝土硬化过程中。由于混凝土失水后干燥，引起体积收缩变形，这种体积变形受到约束时，就可能产生干缩裂缝。混凝土干缩裂缝，一般有三种形状：不规则龟纹状或放射状裂纹，多发生在板、墙的板面部位；每隔一段距离出现一条裂缝，此类裂缝多发生在框架梁、基础梁上面；出现在混凝土现浇板埋管部位的裂缝，沿埋管走向分布。
2水工混凝土裂缝产生的原因：
2.1塑性收缩裂缝
混凝土在凝固的过程中，会逐渐散热和蒸发，这是引起混凝土体积收缩的主要原因，尤其是一些大体积的混凝土。如果混凝土在收缩时受到外界环境的约束，就会自然的形成收缩应力，当这种应力超出当时混凝土极限抗拉强度时，混凝土就会产生裂缝。裂缝是混凝土建筑物最常见的病害之一。裂缝是材料的不连续现象，属于物理性病害，是水工混凝土耐久性的首要影响因素。裂缝的出现，多数在施工期就存在，有的虽然在施工期以后，也多在运行初期5~10年以内，不是由于运行期长工程老化问题，而是早期的问题。裂缝的存在直接导致混凝土抗拉性能的降低，裂缝也会引导有害物质进入混凝土内部，造成钢筋锈蚀，甚至混凝土结构破坏。对于水库蓄水发电和灌溉来说，挡水混凝土结构的裂缝会直接引起渗漏，如果渗漏量达到一定程度，就直接危及工程的蓄水能力；对于混凝土重力坝来说，如果裂缝达到一定贯穿深度和宽度，会引起坝体扬压力的急剧增长，削弱坝体的抗滑能力，对结构抗震非常不利、甚至会对整个坝滑能力，对结构抗震非常不利，甚至会对整个坝体的结构稳定和安全造成威胁。
2.2温差裂缝
温差裂缝是由于混凝土内部和外部之间产生温差所引起的，温差产生的原因是水泥水化热引起的混凝土内部和混凝土表面的温差过大。在温度正负交替过程中，混凝土微孔中的水成为结冰或过冷的水，体积膨胀产生冻胀压力，过冷的水迁移产生渗透压力，当两者的附加作用力超过混凝土的抗拉强度时，混凝土就遭受破坏。温差裂缝主要有三种情况：（1）水工混凝土在施工初期，产生大量的水化热，内外的温差使其产生裂缝；（2）混凝土拆模前后，混凝土表面的温度会急速下降，裂缝产生；（3）由于混凝土内部温度到达极限，但是热量散发慢，而产生温差裂缝。施工中的大体积混凝土，主要是由于温差产生裂缝，诸如水工大坝、分洪闸、拦河坝等体积水工混凝土更易发生此类裂缝。
2.3安定性裂缝
安定性裂缝主要是龟裂，通常是因为混凝土的质量不合格引起的。另外，钢筋因为外界的腐蚀也会引起混凝土裂缝。
3水利施工中混凝土裂缝的处理方式
国内外修补裂缝的方法很多，归纳起来主要有以下三大类
（1）开槽法修补裂缝
该法适合于修补较宽裂缝大于0.5mm，采用环氧树脂10，聚硫橡3，水泥12.5，砂28。首先用人工将晒干筛后的砂、水泥按比例配好搅拌均匀后，将环氧树脂聚硫橡胶也按配比拌匀。然后掺入已拌好的砂、水泥当中，再用人工继续搅拌。最后用少量的丙酮将已拌好的砂浆稀释到适中稠度（约0.4斤丙酮就可以了）。及时将已拌好的改性环氧树脂砂浆用橡胶桶装到已凿好洗净吹干后的混凝土凿槽内进行嵌入。从砂浆开始拌和到嵌入混凝土缝内，一组砂浆的整个施工过程需要30分钟左右完成。嵌入后的砂浆养护即砂浆嵌入缝槽内处理好后两小时以内及时用毛毡、麻袋将聚硫橡胶改性环氧树脂砂浆进行覆盖，待完全初凝后，开始用水养护。
（2）低压注浆法修补裂缝：低压注浆法适用于裂缝宽度为0.2mm~0.3mm的混凝土裂缝修补。修补工序如下：裂缝清理—试漏—配制注浆液—压力注浆—二次注浆—清理表面。当裂缝数量较多时，先要在裂縫位置上贴医用白胶布，再用窄毛刷沾浆沿裂缝来回涂刷封缝，使裂缝封闭，大约10分钟后，揭去胶布条，露出小缝，粘贴注浆嘴用键包严。固化后周边可能有裂口，必须反复用浆补上，以避免注浆漏浆。注浆操作一般在粘嘴的第二天进行，若气温高的话，半天就可注浆。操作时先用补缝器吸取注浆液，插入注浆嘴，用手推动补缝器活塞，使浆液通过注浆嘴压入裂缝，当相邻的嘴中流出浆液时，就可拔出补缝器，堵上铝铆钉。一般由上往下注浆，水平缝一般从一端到另一端逐个注浆。为了保证浆液充满，在注浆后约半小时可以对每个注浆嘴再次补浆。
（3）表面覆盖法修补裂缝
这是一种在微细裂缝（一般宽度小于0.2mm）的表面上涂膜，以达到修补混凝土微细裂缝的目的。分涂覆裂缝部分及全部涂覆两种方法，这种方法的缺点是修补工作无法深入到裂缝内部，对延伸裂缝难以追踪其变化。表面覆盖法所用材料视修补目的及建筑物所处环境不同而异，通常采用弹性涂膜防水材料，聚合物水泥膏、聚合物薄膜（粘贴）等。施工时，首先用钢丝刷子将混凝土表面打毛，清除表面附着物，用水冲洗干净后充分干燥，然后用树脂充填混凝土表面的气孔，再用修补材料涂覆表面。
参考文献：
1、鞠丽艳.混凝土裂缝抑制措施的研究进展.混凝土，2002.5.
2、郭强,胡其辉.混凝土裂缝产生的原因及处理方法[J].水利天地.2010(08)
3、肖健.混凝土裂缝的处理措施[J].中国新技术新产品.2010(24)
4、郝鹏.浅析混凝土变形裂缝的原因[J].辽宁建材.2010(05)
关键字：水利工程 混凝土 裂缝 施工
Abstract: The reservoir dam seepage prevention of general depends on the material and dam concrete crack, new material and new technology, the emergence of basic to eliminate the materials of the phenomenon of the unqualified, and construction conditions of the construction method may not be improper, appears unavoidably tiny cracks in the concrete. Water conservancy project of concrete crack water conservancy project construction influence was unthinkable, only distinguish cracking in concrete of the species, according to the different types of a different reason analysis, according to the water conservancy project construction experience for many years, the corresponding treatment way, summarized a set of mature construction methods, to improve the water conservancy project construction quality has the very vital significance.
Key word: Water conservancy；project construction； concrete； cracks
中图分类号：TV 文献标识码：A 文章编号
小型水库建成前以及建成后，混凝土裂缝都会存在，我们对存在的裂缝不能视而不见，更不能对小型的裂缝置之不理，只有认清混凝土裂缝的种类，针对不同的混凝土裂缝，从形成的原因出发，在水库建成之前，施工过程中，以及后期的维护过程中，三个阶段同时努力，才能达到良好的蓄水能力。
1水工混凝土裂缝的分类
1.1收缩裂缝
（1）表面裂缝
大体积混凝土的内部热量向外散发的较慢，而其外表面与外界接触温度散热速度较快，由于其内部和表面的散热速率不一样，在混凝土的表面会产生一种温度梯度，引发表面产生拉应力，内部产生压应力；如果温差产生的表面拉应力超过此时的混凝土极限抗拉强度，就会在混凝土表面产生裂缝，一般出现在混凝土浇筑后的第3-4天。
（2）贯穿裂缝
混凝土在浇筑数天后由于逐渐降温而产生收缩，再加上混凝土硬化过程中拌合水的水化以及胶质体的胶凝等作用，使得混凝土结构开始收缩，由于受到基底或结构本身的约束，也会产生拉应力，当此拉应力超过混凝土此时的极限抗拉强度，在混凝土结构的薄弱区域就可能产生贯穿裂缝，这种收缩裂缝危害较大。 1.2 塑性塌落裂縫
在混凝土浇筑过程中或者在浇筑初步成型时，都会产生一种塑性塌落裂缝。因为在混凝土的成型过程中，其拌合物中的骨料缓慢下沉，水向上浮，此时钢筋上面的混凝土被钢筋支顶，而钢筋两侧及其下方的混凝土产生下沉，导致混凝土沿钢筋表面产生顺筋裂缝。 1.3 水化热裂缝
水化热裂缝多在大体积混凝土中发生。由于混凝土水化热过高，在凝固过程中释放出大量的水化热，致使混凝土内部温度与混凝土表面温度以及外部环境的温度相差较大，加之有结构自身约束存在，从而产生温度和收缩应力，导致水化热裂缝的产生。通常情况下，大体积混凝土当混凝土内部与表面温度超过24℃，混凝土表面温度与环境温度超过15℃时，最高浇筑温度大于27℃时，则易出现水化热裂缝。 1.4 干缩裂缝
该裂缝多出现在混凝土硬化过程中。由于混凝土失水后干燥，引起体积收缩变形，这种体积变形受到约束时，就可能产生干缩裂缝。混凝土干缩裂缝，一般有三种形状：不规则龟纹状或放射状裂纹，多发生在板、墙的板面部位；每隔一段距离出现一条裂缝，此类裂缝多发生在框架梁、基础梁上面；出现在混凝土现浇板埋管部位的裂缝，沿埋管走向分布。
2水工混凝土裂缝产生的原因：
2.1塑性收缩裂缝
混凝土在凝固的过程中，会逐渐散热和蒸发，这是引起混凝土体积收缩的主要原因，尤其是一些大体积的混凝土。如果混凝土在收缩时受到外界环境的约束，就会自然的形成收缩应力，当这种应力超出当时混凝土极限抗拉强度时，混凝土就会产生裂缝。裂缝是混凝土建筑物最常见的病害之一。裂缝是材料的不连续现象，属于物理性病害，是水工混凝土耐久性的首要影响因素。裂缝的出现，多数在施工期就存在，有的虽然在施工期以后，也多在运行初期5~10年以内，不是由于运行期长工程老化问题，而是早期的问题。裂缝的存在直接导致混凝土抗拉性能的降低，裂缝也会引导有害物质进入混凝土内部，造成钢筋锈蚀，甚至混凝土结构破坏。对于水库蓄水发电和灌溉来说，挡水混凝土结构的裂缝会直接引起渗漏，如果渗漏量达到一定程度，就直接危及工程的蓄水能力；对于混凝土重力坝来说，如果裂缝达到一定贯穿深度和宽度，会引起坝体扬压力的急剧增长，削弱坝体的抗滑能力，对结构抗震非常不利、甚至会对整个坝滑能力，对结构抗震非常不利，甚至会对整个坝体的结构稳定和安全造成威胁。
2.2温差裂缝
温差裂缝是由于混凝土内部和外部之间产生温差所引起的，温差产生的原因是水泥水化热引起的混凝土内部和混凝土表面的温差过大。在温度正负交替过程中，混凝土微孔中的水成为结冰或过冷的水，体积膨胀产生冻胀压力，过冷的水迁移产生渗透压力，当两者的附加作用力超过混凝土的抗拉强度时，混凝土就遭受破坏。温差裂缝主要有三种情况：（1）水工混凝土在施工初期，产生大量的水化热，内外的温差使其产生裂缝；（2）混凝土拆模前后，混凝土表面的温度会急速下降，裂缝产生；（3）由于混凝土内部温度到达极限，但是热量散发慢，而产生温差裂缝。施工中的大体积混凝土，主要是由于温差产生裂缝，诸如水工大坝、分洪闸、拦河坝等体积水工混凝土更易发生此类裂缝。
2.3安定性裂缝
安定性裂缝主要是龟裂，通常是因为混凝土的质量不合格引起的。另外，钢筋因为外界的腐蚀也会引起混凝土裂缝。
3水利施工中混凝土裂缝的处理方式
国内外修补裂缝的方法很多，归纳起来主要有以下三大类
（1）开槽法修补裂缝
该法适合于修补较宽裂缝大于0.5mm，采用环氧树脂10，聚硫橡3，水泥12.5，砂28。首先用人工将晒干筛后的砂、水泥按比例配好搅拌均匀后，将环氧树脂聚硫橡胶也按配比拌匀。然后掺入已拌好的砂、水泥当中，再用人工继续搅拌。最后用少量的丙酮将已拌好的砂浆稀释到适中稠度（约0.4斤丙酮就可以了）。及时将已拌好的改性环氧树脂砂浆用橡胶桶装到已凿好洗净吹干后的混凝土凿槽内进行嵌入。从砂浆开始拌和到嵌入混凝土缝内，一组砂浆的整个施工过程需要30分钟左右完成。嵌入后的砂浆养护即砂浆嵌入缝槽内处理好后两小时以内及时用毛毡、麻袋将聚硫橡胶改性环氧树脂砂浆进行覆盖，待完全初凝后，开始用水养护。
（2）低压注浆法修补裂缝：低压注浆法适用于裂缝宽度为0.2mm~0.3mm的混凝土裂缝修补。修补工序如下：裂缝清理—试漏—配制注浆液—压力注浆—二次注浆—清理表面。当裂缝数量较多时，先要在裂縫位置上贴医用白胶布，再用窄毛刷沾浆沿裂缝来回涂刷封缝，使裂缝封闭，大约10分钟后，揭去胶布条，露出小缝，粘贴注浆嘴用键包严。固化后周边可能有裂口，必须反复用浆补上，以避免注浆漏浆。注浆操作一般在粘嘴的第二天进行，若气温高的话，半天就可注浆。操作时先用补缝器吸取注浆液，插入注浆嘴，用手推动补缝器活塞，使浆液通过注浆嘴压入裂缝，当相邻的嘴中流出浆液时，就可拔出补缝器，堵上铝铆钉。一般由上往下注浆，水平缝一般从一端到另一端逐个注浆。为了保证浆液充满，在注浆后约半小时可以对每个注浆嘴再次补浆。
（3）表面覆盖法修补裂缝
这是一种在微细裂缝（一般宽度小于0.2mm）的表面上涂膜，以达到修补混凝土微细裂缝的目的。分涂覆裂缝部分及全部涂覆两种方法，这种方法的缺点是修补工作无法深入到裂缝内部，对延伸裂缝难以追踪其变化。表面覆盖法所用材料视修补目的及建筑物所处环境不同而异，通常采用弹性涂膜防水材料，聚合物水泥膏、聚合物薄膜（粘贴）等。施工时，首先用钢丝刷子将混凝土表面打毛，清除表面附着物，用水冲洗干净后充分干燥，然后用树脂充填混凝土表面的气孔，再用修补材料涂覆表面。
参考文献：
1、鞠丽艳.混凝土裂缝抑制措施的研究进展.混凝土，2002.5.
2、郭强,胡其辉.混凝土裂缝产生的原因及处理方法[J].水利天地.2010(08)
3、肖健.混凝土裂缝的处理措施[J].中国新技术新产品.2010(24)
4、郝鹏.浅析混凝土变形裂缝的原因[J].辽宁建材.2010(05)