在热液条件下合成了板状的和高度结晶的三八面体蒙脱石。用淬冷玻璃与脱水的钠基蒙脱石分别在(a)500°C,100MPa下1天和11天;(b)300°C,100MPa下7天的条件下进行反应。产物的结晶度和颗粒大小取决于初始玻璃的化学组成,合成温度和热液改性的时间。XRD尖锐的峰和一定相对湿度下水 Platy and highly crystalline trioctahedral smectites were synthesized under hydrothermal conditions. The reaction was performed with quenched glass and dehydrated sodium-based montmorillonite at (a) 500 ° C, 100 MPa for 1 day and 11 days; (b) 300 ° C, 100 MPa for 7 days, respectively. The crystallinity and particle size of the product depend on the initial glass chemistry, synthesis temperature and hydrothermal modification time. XRD sharp peaks and a certain relative humidity of the water