TiO2 particulate photocatalyst anchored on activated carbon fibers (ACFs) was prepared by a molecular adsorption-deposition method. The TiO2 particles deposited on the carbon fibers formed a coating of about 100 nm in thickness. The photocatalyst prepared was characterized by means of SEM, EDS, XRD and UV-vis adsorption spec-troscopy. Anatase-type TiO2 was uniquely developed, and the micrographic structure of ACFs was not damaged during preparation. The roomy space between adjacent carbon fibers could allow UV-light to penetrate into the felt-form photocatalyst to a certain depth, so that a three dimensional environment was formed for the photocatalytic reaction. Such TiO2/ACFs photocatalyst exhibited its photocatalytic reactivity in photodegradation of concentrated methylene blue (MB) solutions. The MB molecules in the bulk solutions was supposed to be condensed around TiO2 particles by ad-sorption by ACFs. Therefore, the photocatalyst possesses the combined effect of adsorption by activated carbon fibers and photocatalytic reactivity of anatase-type TiO2 on MB photodegradation.
TiO2 particulate photocatalyst anchored on activated carbon fibers (ACFs) was prepared by a molecular adsorption-deposition method. The TiO2 particles deposited on the carbon fibers formed a coating of about 100 nm in thickness. The photocatalyst prepared was characterized by means of SEM, EDS Anatase-type TiO2 was uniquely developed, and the micrographic structure of ACFs was not damaged during preparation. The roomy space between adjacent carbon fibers could allow UV-light to penetrate into the felt-form photocatalyst to a certain depth, so that a three dimensional environment was formed for the photocatalytic reaction. Such TiO2 / ACF photocatalyst development its photocatalytic reactivity in photodegradation of concentrated methylene blue (MB) solutions. The MB molecules in the bulk solutions was supposed to be condensed around TiO2 particles by ad-sorption by ACFs. Thus, the photocatalyst possesses the combined effect of adsorption by ac tivated carbon fibers and photocatalytic reactivity of anatase-type TiO2 on MB photodegradation.