【摘 要】
：
1982年3～6月对二炼钢转炉炉壳外表温度变化进行测定表明,炉壳外表温度的高温区多在耳轴处。它与生产实践中耳轴处炉衬易损坏现象相一致。炉壳温度达到400℃时,如不进行有效喷
论文部分内容阅读
1982年3～6月对二炼钢转炉炉壳外表温度变化进行测定表明,炉壳外表温度的高温区多在耳轴处。它与生产实践中耳轴处炉衬易损坏现象相一致。炉壳温度达到400℃时,如不进行有效喷补,此炉衬就基本不能继续使用。炉壳温度测定对鉴别炉衬蚀损程度有一定参考价值。
From March to June of 1982, the change of appearance temperature of the furnace shell of two steel-making converters was measured. It showed that the outer surface temperature of the furnace shell was mostly at the trunnion. It is consistent with the fact that the lining of the trunnion lining is easily damaged in production practice. Furnace shell temperature reaches 400 ℃, if not effective gunning, the lining of the basic can not continue to use. Determination of furnace shell temperature to identify the degree of damage to the lining of a certain reference value.
其他文献
一、1962～1979年美国不锈钢粉的销售情况(见下图)。
First, the United States from 1962 to 1979 stainless steel sales (see below).
1966年,美国人基列普提出以大功率高压脉冲通过电解槽阳极和阴极之间,或通一些辅助电极来提高冰晶石一氧化铝熔体电导率的方法。他的试验之一是,当直流电流为80安培时,槽电
作者近2年来应用双刃刀施行乳癌根治术30例,对防范术后皮瓣坏死和皮下积液取得显著效果,现报告如下。 1 临床资料 1.1 一般资料 双刃刀应用观察组共30例,符合国际分期Ⅰ、Ⅱ
目前我国炼钢电弧炉电能消耗,先进企业吨钢电耗为500度,落后的高达1000度以上,可见节能潜力之大。造成能耗高的原因,主要为某些工艺和设备落后、管理不够完善,以致在电炉生
在回转窑内将铝硅酸盐原料和石灰石、苏打一道烧结以生产氧化铝时,在加热过程中石灰石发生分解,炉料中各组分相互反应,生成碱金属铝酸盐、原硅酸钙及其它化合物。当接近炉料
一、前言查明湿法提纯镍、钴过程中,蒸馏镍(钴)氨液所得的沉淀物组成,对冶金过程的研究是有意义的。 国外对镍盐加碱中和生成的碱式碳酸镍曾进行过不少的研究。据文献报道,
人类染色体8p22-p21.3是前列腺癌常见的基因缺失区,提示在该区域内可能存在1个或多个抑癌基因。Fujiwara等曾在此区域分离到一个命名为PRLTS的候选基因(血小板衍化生长因子
在Н.П.Лякишев和А.Γ.ШАЛИМОВ的著作[1]中对钢的炉外精炼,微合金化,变性处理的方法进行概括,是有益的。著作中特别对金属的深脱硫的方法给予相当多的注意
如何处理钢铁渣,特别是钢渣,已成为当前钢铁工业急待解决的一个迫切问题.成都钢铁厂地处川西平原,年排钢渣万余吨,占地十余亩,与农业争地,矛盾十分尖锐.1979年12月至1980年1
目的:探讨嗜铬细胞瘤的临床特点、诊断方法、治疗及预后。方法:对45例经手术及病理确诊的嗜铬细胞瘤进行分析。结果:嗜铬细胞瘤临床表现复杂多样,但交感神经兴奋及高代谢症群