Semiconductor properties of the passive films formed on 316L and 2205 stainless steel were studied by Electrochemical Impedance Spectroscopy(EIS) in the high-temperature acetic acid.The results showed that the corrosion resistance of 2205 was higher than that of 316L,and the passive films formed on 316L and 2205 stainless steel showed p-type and n-type semiconductor behavior,respectively.Destruction and self-repairing of passive films were studied by using the constant current polarization method.The results showed that for 316L,the self-repairing process would occur when the destruction was lower than the critical extent or it would not do;for 2205,the self-repairing process only happened in a short time when the destruction was in the same extent as 316L.
Semiconductor properties of the passive films formed on 316L and 2205 stainless steel were studied by Electrochemical Impedance Spectroscopy (EIS) in the high-temperature acetic acid. The results showed that the corrosion resistance of 2205 was higher than that of 316L, and the passive films formed on 316L and 2205 stainless steel showed p-type and n-type semiconductor behavior, respectively. Construction and self-repairing of passive films were studied by using the constant current polarization method. The results showed that for 316L, the self-repairing process would occur when the destruction was lower than the critical extent or it would not do; for 2205, the self-repairing process only happened in a short time when the destruction was in the same extent as 316L.