The fly ash cenosphere/AZ91D (FAC/AZ91D) composites containing 5 wt.% and 100 μm in size of fly-ash cenosphere particles were fabricated by means of the compcasting method.The microstructures of the as-cast samples and the effect of the solution treatment at 380℃,400℃,and 420℃ for 16 h on the microstructures of the samples were investigated by using of OM,SEM,XRD and EDS.The results showed that the cenospheres distributed homogeneously in the Mg alloy,and were almost filled with Mg alloy.The main interfacial phase between the cenospheres and AZ91D Mg alloy was identified as MgAl2O4 according to XRD,EDS and thermodynamic analysis.Mg2Si particles tended to be spheroidized via the solution treatment and the β phase (Mg17Al12) dissolved completely at 400℃.
The fly ash cenosphere / AZ91D (FAC / AZ91D) composites containing 5 wt.% And 100 μm in size of fly-ash cenosphere particles were fabricated by the method of the compcasting. The microstructures of the as-cast samples and the effect of the solution treatment at 380 ° C, 400 ° C, and 420 ° C for 16 h on the microstructures of the samples were investigated by using of OM, SEM, XRD and EDS. The results showed that the cenospheres distributed homogeneously in the Mg alloy, and were almost filled with Mg alloy. Main interfacial phase between the cenospheres and AZ91D Mg alloy was identified as MgAl2O4 according to XRD, EDS and thermodynamic analysis. Mg2Si particles tended to be spheroidized via the solution treatment and the beta phase (Mg17Al12) dissolved completely at 400 ℃.