Various VOx/SiO2 catalysts were prepared by the methods of physical mixing, conventional wetness impregnation and ultrasonication-assistant impregnation. The catalysts were characterized by XRD, UV-Vis DRS, Raman, TPR, ESR and TPSR techniques and the nature of the vanadium species were correlated to their catalytic performance in the reaction of direct conversion of methane to formaldehyde. It is concluded that highly dispersed monomeric and low oligomeric vanadia species are formed on the sample prepared with both traditional wetness impregnation method and ultrasonication-assistant impregnation, whereas in the latter case, the amount of oligomeric vanadia species is much smaller. The V2O5 microcrystallines are the dominant species on the material prepared by physical mixing method. During the selective oxidation of methane, VⅤspecies are reduced to VⅣparamagnetic species and both microcrystalline A2O5 species and oligomeric vanadia species are found to further disperse and transform into tetrahedral vanadia species. Based on the results of UV Raman spectroscopy and TPSR, CO2 is suggested to be formed via two different routes, in which one is from the sequence reaction of CH4→HCHO →CO→CO2 over monomeric vanadia species, and the other is from the direct oxidation of methane to CO2 over oligomeric vanadia species. Oligomeric vanadia species is more active than monomeric vanadia species for methane activation. Various VOx / SiO2 catalysts were prepared by the methods of physical mixing, conventional wetness impregnation and ultrasonication-assistant impregnation. The catalysts were characterized by XRD, UV-Vis DRS, Raman, TPR, ESR and TPSR techniques and the nature of the vanadium species were correlated to their catalytic performance in the reaction of direct conversion of methane to formaldehyde. It is conclusion that highly dispersed monomeric and low oligomeric vanadia species are formed on the sample prepared with both traditional wetness impregnation method and ultrasonication-assistant impregnation, but in in the latter case, the amount of oligomeric vanadia species is much smaller. The V2O5 microcrystallines are the dominant species on the material prepared by physical mixing method. The V2O5 microcrystallines are the dominant species on the material prepared by physical mixing method. species are found to further disperse and transf Based on the results of UV Raman spectroscopy and TPSR, CO2 is suggested to be formed via two different routes, in which one is from the sequence reaction of CH4 → HCHO → CO → CO2 over monomeric vanadia species, and the other is from the direct oxidation of methane to CO2 over oligomeric vanadia species. Oligomeric vanadia species is more active than monomeric vanadia species for methane activation.