【摘 要】
：
The high performance magnesium alloy was investigated by adding B2O3 in magnesium and magnesium alloys. Experiments include adding B2O3 in Mg, Mg-Al and Mg-RE a
【机 构】
：
Graduate School of Science and Technology,Machinery and Electronic Engineering Institute,Department
论文部分内容阅读
The high performance magnesium alloy was investigated by adding B2O3 in magnesium and magnesium alloys. Experiments include adding B2O3 in Mg, Mg-Al and Mg-RE alloys, respectively, studying the effects of B2O3 on the microstructure, were studied measuring the change of grain size and microhardness of the materials, discussing the change of grain size, morphology and distribution. The results show that adding 3% or 6%(mass fraction) B2O3 in Mg can bring twinning in Mg, adding B2O3 in Mg-Al alloys and Mg-RE alloys can refine the alloy grain size. Adding 3%B2O3 in Mg-6Al alloys can refine the average grain size by about 5 μm, with the average hardness increased by 13.3% (53.3-60.4 HV0.03); adding 6%B2O3 in Mg-6Al alloys can refine the average grain size by about 13 μm, with the average hardness increased by 15.8% (53.3-61.73 HV0.03); adding 3% and 6%B2O3 into Mg-6RE alloys can refine the grain size by about 5 and 9 μm, respectively, with the average hardness decreased to HV0.03 64.66 and HV0.03 57.86, respectively from HV0.03 88.57. In the Mg-6Al alloy the content of aluminum is increased, while in the Mg-6RE alloy the content of oxygen is decreased. It can be concluded that it is beneficial to develop Mg-Al-B-O particle reinforce composite alloys , and it is feasible to develop nanometer crystallization of block material by Mg-B-O-RE.
其他文献
In Nb-Si based alloys with a two-phase NbSS/ intermetallic Nb5Si3 structure, the Nb5Si3 provides high-temperature strength, while the Nb solid-solution phase, N
The formation mechanism of bulge on the works surface during the extrusion process was analyzed. The bulges size and the reasons for abscission were studied. Th
30%Al2O3p/Al-Cu-2.0Mg composite and Al2O3p/Al-Cu-2.5Mg composite with 0.3 μm-Al2O3 particles were fabricated.Age-hardening behaviors of two composites and the
The technology of length-alterable line-scanning laser sintering was introduced. Based on the research of laser heating property,powder thermal physics paramete
Based on initial discontinuity state (IDS) of material, a preliminary analytical model was presented to evaluate the effect of interaction of pitting corrosion
A kind of aluminum cooler was manufactured by means of vacuum brazing technique, and the cooler was examined by hydraulic pressure test. The result indicates th
The titanium dioxide sols were synthesized with tetrabutyl titanate as precursor,diethanolamine(DEA) as complexing agent ,polyethylene glycol (PEG) as organic t
Half-metallic Fe3O4 films prepared by DC magnetron reactive sputtering with a tantalum(Ta) buffer layer was investigated. Primary emphasis is placed on the stru
In this paper, the authors present the transmission line (TL) realization of one-dimensional subwavelength resonator formed by a pair of conventional right-hand
In situ A356/TiB2 composites were successfully fabricated via in-melt reaction among aluminium alloy, K2TiF6 and KBF4 compounds. The composite was examined by u