用盖革计数管X光衍射方法定量地测定了热轧及在α相区内冷轧铀棒的择优取向。测量结果表明,轻微压下的热轧使010面强烈地取垂直于轧向的方向,而110面微弱地取此方向。而进一步热轧使110面强烈地取垂直于轧向的方向,而010面微弱地取此方向。轻微冷轧使010面强烈地取垂直于轧向的方向。而130面轻微地取此方向。
Geiger count tube X-ray diffraction method was used to quantitatively determine the hot rolling and the preferred orientation of the cold-rolled uranium rod in the α-phase region. The measurement results show that hot rolling with a slight pressure causes the surface of 010 to strongly take a direction perpendicular to the rolling direction and the surface of 110 weakly take this direction. Further hot rolling makes the 110 surface strongly perpendicular to the rolling direction, while the 010 surface weakly takes this direction. Slightly cold-rolled so that the surface 010 strongly taken perpendicular to the rolling direction. While 130 faces take this direction slightly.