This study presents a novel method using a disk-like sample to assess the workability of metal during the cross wedge ro......
Experimental Study of Lightweight Expanded Polystyrene Aggregate Concrete Containing Silica Fume and
...
Six representative parent rocks of sand, including limestone, quartzite, gneisses, granite, Basalt and Marble were selec......
...
Making full use of reclaimed asphalt pavement(RAP)can ensure sustainable development of highway construction,so it is ne......
This study aims to use recycled fine aggregate(RFA)sourced from construction waste as a component material in producing ......
The Influence of the Admixed Micelles Based on Triblock Copolymers on Material Properties of Both Fr
In this study, the influence of the micelles prepared by triblock copolymers on the properties of fresh and hardened cem......
The production and use of efficient blended cements is state-of-the-art.Besides numerous technical advantages,these ceme......
Experimental Study on Performances of Self-compacting Backfill Material Utilizing Rapid Hardening Su
Using rapid hardening sulphoaluminate cement and recycled fine aggregate of construction waste for producing a new kind ......
The effect of two kinds of ground limestone fillers on workability and the strength development of cement and the concre......
High performance alkali-activated slag pavement concrete (ASC) was prepared by adding Na2SiO3 and NaOH complex activator......
This study was focused on developing concrete using alkali-activated copper slag(AACS)as a binder.The properties of alka......
According to the preferred109selection of the raw materials and the optimization of the mix proportioning,low viscos......
目的：完善和健全护士知识、技能巩固、提高和发展，培养高素质护理人才。方法针对培养对象的不同建立并实施新护士岗前培训，见习护士规......
,Evaluation of asphalt mixture behavior incorporating warm mix additives and reclaimed asphalt pavem
Incorporation of warm mix asphalt (WMA) and reclaimed asphalt pavement (RAP) has benefited the asphalt industry in many ......
This study systematically compared the influences of yttrium(Y),boron(B),and carbon(C) on the microstructural refinement......
探讨了纳米SiO2和PVA纤维掺量及石英砂粒径对水泥基复合材料工作性和抗压强度的影响.结果表明,随着纳米SiO2和PVA纤维体积掺量的增......
The permeability,alkali-silica reaction,workability and strength of GHPC(green high performance concrete) were studied i......
Improved cold rolling workability of warm rolled Fe-6.5wt％Si electrical steel with columnar grains b
The effects of annealing temperature(with the annealing time being constant at 1 h) on the microstructure, ordering, res......
Aluminium-based metal matrix composites were synthesized from Al-TiO2-Gr powder mixtures using the powder metallurgy tec......
通过微观组织和固有内在缺陷观察，研究了加工方法对 ZK60A 变形镁合金加工性能的影响。利用半连续铸造、半连续铸造后挤压及模具铸......
为了研究聚丙烯纤维对橡胶混凝土工作性能及力学性能的影响,选取橡胶置换率5%和25%的混凝土作为基础试验,按纤维掺量为0、0.3、0.6......
结合国内外关于建筑垃圾中废砖磨细制成废砖粉的活性研究现状,对废砖粉的应用研究、活性机理研究、活性激发研究进行综述,总结影响......
采用粉煤灰取代40%水泥来制备粉煤灰自密实混凝土(SCC),研究其工作性、基本力学性能和轴压变形性能随钢纤维体积分数的变化规律.结......
机制砂的级配、细度模数、石粉含量、亚甲蓝(MB)值、有害物质含量等品质指标对混凝土性能产生重要影响。文中以花岗岩机制砂为细集......
对于偏高岭土和海泡石在复掺条件下对水泥净浆强度与微结构的影响进行了系统研究。分别探讨了偏高岭土和海泡石在单掺与复掺状态下......
研究了纳米SiO2对污泥焚烧灰-水泥复合胶凝体系性能的影响,并对其水化程度进行了分析。结果表明:随着污泥焚烧灰掺量的增加,复合胶......
平江抽水蓄能电站泵送混凝土使用的花岗岩为主的人工细骨料,云母含量较高。通过分选工艺降低游离云母的机制砂配制混凝土,性能试验......
为了解决地铁盾构管片施工过程中渗水问题,研究立足于天津地铁项目,综合现有高性能混凝土配合比的设计经验,采用控制变量的方法,设......
本文分析了目前农村公路的发展以及维护现状,指出水泥混凝土和热拌沥青混凝土在公路修补中的不足,进而提出冷拌沥青混凝土用于农村......
阐述了掺粉煤灰对新拌混凝土的和易性以及坍落度经时变化的影响，并为解决实际应用问题提供了思路。......
本试验以兰州某工地废弃混凝土为原料来制备再生粗骨料,配制4组不同配合比,且每组分别以粗骨料取代率为0%,30%,70%,100%而制作96个......
水泥混凝土增强剌是一种新型的混凝土外加剂，在保证混凝土性能的前提下，可降低胶凝材料的用量。本文系统研究了HX水泥混凝土增强剂对......
以上海铁路南站9.9m平台混凝土的施工特殊性为出发点,从混凝土性能入手,开发出适合工程施工需要的混凝土产品,获得成功。......
自密实混凝土是一种具有高工作性能的高性能混凝土。探讨了自密实混凝土工作性能的评定方法,并对掺加磨细矿渣的自密实混凝土进行......
为满足预制构件实际生产需要,提高生产效率并节约成本,使用普通硅酸盐水泥（OPC）和低碱硫铝酸盐水泥（SAC）配制了便于施工、满足早强早脱......
针对自密实混凝土工作性评价问题,基于新拌自密实混凝土质量控制要求及模糊数学原理,提出了自密实混凝土工作性模糊综合评判方法（FE......
简介了不定形耐火材料在材质，结合方式，作业性能和调和用水量方面的发展趋势；叙述了自结合自烧结和自流型不定形耐火材料的特性和优点......
水泥基复合材料均为抗拉性能低的脆性物质,加入随机分布的纤维会显著提高其断裂强度,素混凝土在加入纤维后会破坏原有的颗粒状骨架......
通过蔡因煤矿陷落柱的成因及充水性分析，提出了3煤、12下、16、17煤层中发育陷落柱采区的可采性的防治水依据。......
本文探讨了外加剂、矿物掺合料、环境温湿度等因素对超缓凝混凝土性能的影响，试验数据结果：混凝土凝结时间随着超缓凝剂掺量增加而延......
将经改性的高岭土尾矿与水晶废渣复合，等量取代水泥内掺到水泥基材料中，研究了掺入前后和不同掺量对水泥基材料的工作性、力学性能和......
研究了粉煤灰掺量、粗骨料孔隙率、砂率、外加剂等因素对低强度等级自密实混凝土工作性能的影响规律。结果表明：适当降低水泥用量,......
混凝土是土木工程建设众多材料中最主要、也是最重要的材料之一,它应用范围广泛,并且用量比较大。混凝土作为一种重要的建筑材料,......
以C50预制箱梁所用的高性能混凝土为例,阐述试验来分析碎石的最大粒径、碎石级配、石粉含量三个材料指标对高性能混凝土工作性能的......
石粉含量的变化对机制砂混凝土强度的影响情况比较复杂,因此通过将石粉含量不同的机制砂掺入C30和C50混凝土,研究石粉含量对不同强......
在固定CON80减水剂掺量的前提下，调整粉煤灰掺量设计5组配比，开展本课题所研究的混凝土配比设计工作，并完成试验研究，在对所测得的实验......
在固定KS-2减水剂掺量的前提下,调整粉煤灰掺量设计5组配比,进行高性能混凝土的配合比设计与试验研究,通过对实验数据的整理和分析......
文章应用层次分析法的基本原理，针对新拌自密实混凝土工作性的主要因素，构建了自密实混凝土配合比方案综合评价和优选模型，并应用模型......