【摘 要】
:
The wrought Al-Mg alloys, commercially designated as 5000 series, have been widely applied as a form of sheet or plate to various industries such as automotive, shipbuilding, construction, beverage ca
【机 构】
:
Korea Institute of Industrial Technology, Korea
【出 处】
:
15th International Conference on Aluminium Alloys(ICAA15)(第十
论文部分内容阅读
The wrought Al-Mg alloys, commercially designated as 5000 series, have been widely applied as a form of sheet or plate to various industries such as automotive, shipbuilding, construction, beverage can, etc., because they have good formability, weldability, corrosion resistance together with wide range of controllable strength.Most sheet and plate of aluminum alloys is traditionally fabricated through series of processes including DC casting, homogenization, hot-rolling, inter-final-annealing and cold-rolling, roughly.The required temper and mechanical properties of a product have to be made in the final pass of cold-rolling or annealing process.
其他文献
Wire-Arc Additive Manufacturing (WAAM) is highly efficient, can achieve high deposition rates and does not rely on expensive equipment.WAAM thus has the potential to produce large scale, near net-shap
In this study we focused on the influence of nano-size B4C particles (~60 nm) on microstructure and mechanical behavior of Al-2024/B4C composites.The experiment involved ball milling of 2024-Al and B4
Al-Zn-Mg alloys are widely used in aircraft and automotive industries for structure components because of exceptionally high specific strength in the fully aged condition.Precipitation sequence for Al
Dispersoids play a significant role in the recrystallization and texture development for wrought Al-Mg-Si (6xxx series) alloys by inhibiting grain boundary motion.It is therefore important to understa
Al-7 wt% Si ahoy was treated by the high pressure solution (2 GPa) and natural aging, and precipitation behavior of the dispersoids in the alloy was investigated through TEM to provide a possible form
In this study the influence of natural aging in energy absorbance capacity of 6xxx series extruded profiles after artificial aging is examined by means of optical and scanning electron microscopy, qua
The solution process of a Al-Mg-Si alloy is heated by electric resistance wire and hot air respectively.Specimens were performed at 560℃ for 30 min and then cooled by water quenching.Immediately, the
In this paper, 40 mm thick A7N01-T5 aluminum alloy plate was friction stir welded using a double side process.The microstructure evolution of different zones of the joint, which is significantly affec
In recent years, energy saving and environmental protection have caused widespread concern.Using the aluminum alloys for the vehicle can reduce the weight of the vehicle to reduce energy consumption.6
The recrystallization kinetics at 530℃ of twin roll casting Al-Mn alloys with and without low temperature pre-recovery was investigated.It was revealed that the samples with/without pre-recovery exhib