【摘 要】
：
Monoclinic LaPO4 nanostructures with uniform rod shape have been successfully synthesized by a simple sol-gel method. The procedure involves formation of homoge
【机 构】
：
School of Chemistry and Chemical Engineering,State Key Laboratory of Powder Metallurgy
论文部分内容阅读
Monoclinic LaPO4 nanostructures with uniform rod shape have been successfully synthesized by a simple sol-gel method. The procedure involves formation of homogeneous, transparent, metal-citrate-EDTA gel precursors, followed by calcination to promote thermal decomposition of the gel precursors to yield the LaPO4 nanoparticles. Their morphologies and structures were characterized by XRD, TEM, TG-DSC and HRTEM. The results indicate that single monoclinic phase LaPO4 nanorods are readily obtained at 800 ℃ within 3 h. Furthermore, photoluminescence (PL) characterization of the Eu3+-doped LaPO4 nanocrystals was carried out. The effects of calcination temperatures and Eu3+ doping content on the PL properties were elaborated in detail. Room-temperature photoluminescence (PL) characterization reveals that the optical brightness as well as the intensity ratio of 5D0-7F1 to 5D0-7F2 is highly dependent on the calcination temperature, and the Eu0.05La0.95PO4 nanophosphor shows the relatively promising PL performance with the most intense emission.
其他文献
Using solid-state synthesis method,a series of samples of lanthanum doped Li1-xLaxFePO4(x=0.0025,0.005,0.0075,0.01)were prepared.Each cathode structural and ele
In order to obtain the thermodynamic description of the Mg-Ga binary system, the thermodynamic assessment of the system was carried out using the CALPHAD method
The microstructure and properties of the 93W-4Ni-2Co-1Fe (mass fraction, %) tungsten heavy alloys prepared by mechanical alloying and electric current activated
With the development of aero-engine,gas import temperatures of hot section structural materials are increasingly higher.Metal alloy materials due to the rapidly
We investigated the transport properties of isoelectronic substitution of Yb by Ca for Zintl phase YbCd2Sb2 below 300 K.The p-type Yb1-xCaxCd2Sb2(0.2≤x≤0.8)sa
The β-SiC/SiO2 core-shell nanowires with the "stem-and-node" structure were synthesized in the presence of cerium oxide by the carbothermal reduction of the st
Single crystals of LaP3O9·3H2O were prepared using a classical method of aqueous chemistry whereas those of the ultraphosphate LaP5O14 were obtained by flux me
High cycle fatigue behavior of die cast AZ91D magnesium alloy with different Nd contents was investigated.Axial mechanical fatigue tests were conducted at the s
In view of high strength and poor impact toughness of the high-zinc magnesium alloys, the method of micro-alloying was adopted to improve the impact-toughness o
Melt-spun Nd4.5Fe4.5B18.5 ribbons were prepared under various superheat temperatures.The microstructure characteristics,crystallization behavior,and subsequent