The adsorption and diffusion behavior of Cl~- on sputtering Fe-20 Cr nanocrystalline(NC) thin film compared with corresponding coarse crystalline(CC) alloy has been studied in HCl + NaCl solution(pH = 2,[Cl~-]=0.1 mol/L) by electrochemical techniques,X-ray photoelectron spectroscopy(XPS) and the firstprinciples calculations.The XPS results show that adsorption and diffusion of Cl~- in the passive film has been inhibited on NC thin film.Ultra-violet photoelectron spectroscopy(UPS) results show that the work function Φ_s of NC thin film(4.7 eV) is higher than that of CC alloy(4.5 eV).The theoretical calculations and valence electron structure analysis were used to understand the effect of nanocrystallization in this work.
The adsorption and diffusion behavior of Cl ~ - on sputtering Fe-20 Cr nanocrystalline (NC) thin film compared with corresponding coarse crystalline (CC) alloy has been studied in HCl + NaCl solution (pH = 2, mol / L) by electrochemical techniques, X-ray photoelectron spectroscopy (XPS) and the firstprincipal calculations. XPS results show that adsorption and diffusion of Cl ~ - in the passive film has been inhibited on NC thin film. Ultra-violet photoelectron spectroscopy (UPS) results show that the work function Φ_s of NC thin film (4.7 eV) is higher than that of CC alloy (4.5 eV). The theoretical calculations and valence electron structure analysis were used to understand the effect of nanocrystallization in this work.