The effect of extrusion on grain refinement has been studied in the AZ91 cast ingots. It is found that grain sizesmaller than 10μm can be obtained by the extrusion processing. Vickers hardness measurements were also carriedout to evaluate the effect of these processes on the room temperature mechanical properties. The experimentalresults of high temperature tensile tests revealed that the stress was inversely proportional to the square of the grainsize and that the activation energy for superplastic flow was higher than that for grain boundary diffusion.
The effect of extrusion on grain refinement has been studied in the AZ91 cast ingots. It is found that grain sizesmaller than 10μm can be obtained by the extrusion processing. Vickers hardness measurements were also carriedout to evaluate the effect of these processes on the room temperature mechanical the experimental results of high temperature tensile tests revealed that the stress was inversely proportional to the square of the grainsize and that the activation energy for superplastic flow was higher than that for grain boundary diffusion.